Color-stabilized electrochromic devices

ABSTRACT

An electrochromic medium for use in a normally operating electrochromic device comprising an anodic material and a cathodic material wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic, an additive, and means associated with the additive for maintaining a colorless or nearly colorless electrochromic medium while the electrochromic medium is in a high transmission state relative to an electrochromic medium without the additive.

CROSS-REFERENCE TO RELATED APPLICATION(S)

This application is a continuation of U.S. application Ser. No. 09/377,455, filed Aug. 19, 1999, now U.S. Pat. No. 6,188,505.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates in general to electrochromic devices, and more particularly, to normally operating, color-stabilized electrochromic devices having an electrochromic medium comprising one or more additives, which serve to substantially preclude the formation of undesirable residual color within the electrochromic medium while in its high transmission state.

2. Background Art

Electrochromic devices have been known in the art for several years. While the utilization of electrochromic devices, such as electrochromic mirrors, has become increasing popular among, for example, the automotive industry, the development of undesirable residual color within the electrochromic medium remains problematic.

Indeed, when a sufficient electrical potential difference is applied across the electrodes of a conventional device, the electrochromic medium becomes intentionally colored (i.e. a low transmission state) inasmuch as one or more of the anodic and the cathodic materials are oxidized and reduced, respectively. Specifically, the anodic materials are oxidized by donating electrons to the anode, and the cathodic materials are reduced by accepting electrons from the cathode.

For most commercially available devices, when the electrical potential difference is removed or substantially diminished, the anodic and cathodic materials return to their native or unactivated state, and in turn, return the electrochromic medium to its colorless or nearly colorless state (i.e. a high transmission state). The application and removal of an electrical potential difference is conventionally known as a single cycle of the electrochromic device.

Scientists have observed that over a period of cycles and/or time, during normal operation of the electrochromic device, the electrochromic medium sometimes does not remain colorless in the high transmission state. In some instances, even in the absence of an electrical potential difference, either one or both of a portion of the anodic and cathodic materials are oxidized or reduced respectively, thereby forming residual oxidized and/or reduced materials. The residual oxidized anodic materials and/or the residual reduced cathodic materials of the electrochromic medium can result in an undesired residual coloration of the electrochromic medium.

Factors that are believed to facilitate the formation of the undesired residual oxidized anodic and/or reduced cathodic materials include, among other things, impurities within the medium, thermal and/or photochemical decomposition of one or more of the medium materials, and/or the permeation of water and/or oxygen into the electrochromic medium.

It is therefore an object of the present invention to provide an electrochromic medium with a color-stabilizing additive that remedies the aforementioned detriments and/or complications associated with maintaining a colorless or nearly colorless electrochromic device while the device is in its high transmission state.

SUMMARY OF THE INVENTION

The present invention is directed to an electrochromic medium for use in a normally operating electrochromic device comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) an additive, wherein the additive is more easily reduced than the cathodic material.

In a preferred embodiment of the invention, the additive substantially precludes the formation of a residual reduced cathodic material while the electrochromic medium is in a high transmission state.

In another preferred embodiment of the invention, the additive comprises either an oxidized form of the anodic material or an additional material present in an oxidized form.

The present invention is also directed to an electrochromic medium for use in a normally operating electrochromic device comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) an additive, wherein the additive comprises a reduced form of the cathodic material.

The present invention is further directed to an electrochromic medium for use in a normally operating electrochromic device comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) an additive, wherein the additive is more easily oxidized than the anodic material, and wherein the additive is selected from the group comprising substituted ferrocenes, substituted ferrocenyl salts, and mixtures thereof.

The present invention is also directed to an electrochromic medium for use in a normally operating electrochromic device comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) an additive, wherein the additive comprises (1) a first component that is more easily reduced than the cathodic material and (2) a second component that is more easily oxidized than the anodic material.

In a preferred embodiment of the invention, the first component substantially precludes the formation of a residual reduced cathodic material and the second component substantially precludes the formation of a residual oxidized anodic material while the electrochromic medium is in a high transmission state.

In another preferred embodiment of the invention, the first component comprises either an oxidized form of the anodic material or an additional electroactive material present in an oxidized form.

The present invention is additionally directed to an electrochromic medium for use in a normally operating electrochromic device comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; (b) an additive; and (c) means associated with the additive for maintaining a colorless or nearly colorless electrochromic medium while such a medium is in a high transmission state relative to an electrochromic medium without the additive.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will now be described with reference to the drawings wherein:

FIG. 1 of the drawings is a cross-sectional schematic representation of an electrochromic device fabricated in accordance with the present invention;

FIG. 2 of the drawings is a two-dimensional plot showing the change in a* value as a function of exposure time to an oxidative environment for Experiments 1A-1B;

FIG. 3 of the drawings is a two-dimensional plot showing the change in b* value as a function of exposure time to an oxidative environment for Experiments 1A-1B;

FIG. 4 of the drawings is a two-dimensional plot showing the change in a* value as a function of exposure time to an oxidative environment for Experiments 2A-2D;

FIG. 5 of the drawings is a two-dimensional plot showing the change in b* value as a function of exposure time to elevated temperatures for Experiments 2A-2D;

FIG. 6 of the drawings is a two-dimensional plot showing the change in a* value as a function of exposure time to elevated temperatures for Experiments 3A-3B;

FIG. 7 of the drawings is a two-dimensional plot showing the change in b* value as a function of exposure time to elevated temperatures for Experiments 3A-3B;

FIG. 8 of the drawings is a two-dimensional plot showing the change in a* value as a function of exposure time to elevated temperatures for Experiments 4A-4B; and

FIG. 9 of the drawings is a two-dimensional plot showing the change in b* value as a function of exposure time to elevated temperatures for Experiments 4A-4B.

DETAILED DESCRIPTION OF THE INVENTION

Referring now to the drawings and to FIG. 1 in particular, a cross-sectional schematic representation of electrochromic device 100 is shown, which generally comprises first substrate 112 having a front surface 112′ and a rear surface 112,″ second substrate 114 having a front surface 114′ and a rear surface 114,″ and chamber 116 for retaining electrochromic medium 124. It will be understood that electrochromic device 100 may comprise, for illustrative purposes only, a mirror, a window, a display device, a contrast enhancement filter, and the like. It will be further understood that FIG. 1 is merely a schematic representation of electrochromic device 100. As such, some of the components have been distorted from their actual scale for pictorial clarity. Indeed, numerous other electrochromic device configurations are contemplated for use, including those disclosed in U.S. Pat. No. 5,818,625, which is hereby incorporated by reference in its entirety.

First substrate 112 may be fabricated from any one of a number of materials that are transparent or substantially transparent in the visible region of the electromagnetic spectrum, such as, for example, borosilicate glass, soda lime glass, float glass, natural and synthetic polymeric resins or plastics including Topas®, which is commercially available from Ticona of Summit, N.J. First substrate 112 is preferably fabricated from a sheet of glass having a thickness ranging from approximately 0.5 millimeters (mm) to approximately 12.7 mm. Of course, the thickness of the substrate will depend largely upon the particular application of the electrochromic device. While particular substrate materials have been disclosed, for illustrative purposes only, it will be understood that numerous other substrate materials are likewise contemplated for use—so long as the materials are at least substantially transparent and exhibit appropriate physical properties, such as strength to be able to operate effectively in conditions of intended use. Indeed, electrochromic devices in accordance with the present invention can be, during normal operation, exposed to extreme temperatures as well as exposed to substantial UV radiation, emanating primarily from the sun.

Second substrate 114 can be fabricated from similar materials as that of first substrate 112. However, if the electrochromic device is a mirror, then the requisite of substantial transparency is not necessary. As such, second substrate 114 may, alternatively, comprise polymers, metals, glass, and ceramics—to name a few. Second substrate 114 is preferably fabricated from a sheet of glass having a thickness ranging from approximately 0.5 mm to approximately 12.7 mm. If first and second substrates 112 and 114, respectively, are fabricated from sheets of glass, then the glass can optionally be tempered prior to or subsequent to being coated with layers of electrically conductive material (118 and 120).

One or more layers of electrically conductive material 118 are associated with rear surface 112″ of the first substrate. These layers serve as an electrode for the electrochromic device. Electrically conductive material 118 is desirably a material that: (a) is substantially transparent in the visible region of the electromagnetic spectrum; (b) bonds reasonably well to first substrate 112; (c) maintains this bond when associated with a sealing member; (d) is generally resistant to corrosion from materials contained within the electrochromic device or the atmosphere; and (e) exhibits minimal diffusion or specular reflectance as well as sufficient electrical conductance. It is contemplated that electrically conductive material 118 may be fabricated from fluorine doped tin oxide (FTO), for example TEC glass, which is commercially available from Libbey Owens-Ford-Co., of Toledo, Ohio, indium doped tin oxide (ITO), doped zinc oxide or other materials known in the art.

Electrically conductive material 120 is preferably associated with front surface 114′ of second substrate 114, and is operatively bonded to electrically conductive material 118 by sealing member 122. As can be seen in FIG. 1, once bonded, the sealing member and the juxtaposed portions of electrically conductive materials 118 and 120 serve to define the inner peripheral geometry of chamber 116.

Electrically conductive material 120 may vary depending upon the intended use of the electrochromic device. For example, if the electrochromic device is a mirror, then the material may comprise a transparent conductive coating similar to electronically conductive material 118 (in which case a reflector is associated with rear surface 114″ of second substrate 114). Alternatively, electrically conductive material 120 may comprise a layer of reflective material in accordance with the teachings of U.S. Pat. No. 5,818,625. In this case, electrically conductive material 120 is associated with front surface 114′ of second substrate 114. Typical coatings for this type of reflector include chromium, rhodium, silver, silver alloys, and combinations thereof.

Sealing member 122 may comprise any material that is capable of being adhesively bonded to the electronically conductive materials 118 and 120 to, in turn, seal chamber 116 so that electrochromic medium 124 does not inadvertently leak out of the chamber. As is shown in dashed lines in FIG. 1, it is also contemplated that the sealing member extend all the way to rear surface 112″ and front surface 114′ of their respective substrates. In such an embodiment, the layers of electrically conductive material 118 and 120 may be partially removed where the sealing member 122 is positioned. If electrically conductive materials 118 and 120 are not associated with their respective substrates, then sealing member 122 preferably bonds well to glass. It will be understood that sealing member 122 can be fabricated from any one of a number of materials including, for example, those disclosed in U.S. Pat. Nos. 4,297,401, 4,418,102, 4,695,490, 5,596,023, 5,596,024, 4,297,401, and U.S. patent application Ser. No. 09/158,423, now U.S. Pat. No. 6,157,480, entitled “Improved Seal For Electrochromic Devices,” all of which are herein incorporated by reference.

For purposes of the present disclosure the electrochromic medium is disclosed herein below as being a solution phase medium. However, it will be understood that hybrid media and solid state media are likewise contemplated for use. In a hybrid medium, one of the anodic or cathodic materials can be applied (in a solid form) to its respective electrically conductive material. For example, a cathodic material, such as tungsten oxide (WO₃) can be applied onto the surface of a conventional electrically conductive material. In a solid state medium both of the anodic and cathodic materials can be applied in a solid form to their respective substrates. In such an embodiment, the additive may still be dissolved in the electrolyte positioned between the anodic and cathodic materials.

Electrochromic medium 124 is shown in FIG. 1, which generally comprises an anodic material, a cathodic material, and a color-stabilizing additive dissolved in at least one solvent. During normal operation of device 100, the color-stabilizing additive enables the electrochromic medium 124 to remain colorless or nearly colorless in the high transmission state. Typically both of the anodic and cathodic materials are electroactive and at least one of them is electrochromic. Regardless of its ordinary meaning, the term “electroactive” will be defined herein as a material that undergoes a modification in its oxidation state upon exposure to a particular electrical potential difference. Additionally, the term “electrochromic” will be defined herein, regardless of its ordinary meaning, as a material that has a change in its extinction coefficient at one or more wavelengths upon exposure to a particular electrical potential difference.

The cathodic material may include, for example, viologens, such as methyl viologen tetrafluoroborate or octyl viologen tetrafluoroborate. It will be understood that the preparation of the above-identified viologens is well known in the art. While specific cathodic materials have been provided, for illustrative purposes only, numerous other conventional cathodic materials are likewise contemplated for use including, but by no means limited to, those disclosed in U.S. Pat. No. 4,902,108, which is hereby incorporated in its entirety by reference. Indeed, the only contemplated limitation relative to the cathodic material is that it should not adversely affect the electrochromic performance of the device 100. Moreover, it is contemplated that the cathodic material may comprise a solid transition metal oxide, including, but not limited to, tungsten oxide.

The anodic material may comprise any one of a number of materials including ferrocene, substituted ferrocenes, substituted ferrocenyl salts, phenazine, substituted phenazines, phenothiazine, substituted phenothiazines. Examples of anodic materials may include di-tert-butyl-diethylferrocene, (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate, (3-(tetra-tert-butylferrocenyl)propyl)triethylammonium tetrafluoroborate, 5,10-dimethylphenazine, and 3,7,10-trimethylphenothiazine. It will be understood that numerous other anodic materials are contemplated for use including those disclosed in the previously referenced and incorporated '108 patent.

For illustrative purposes only, the concentration of the anodic and cathodic materials can range from approximately 1 mM to approximately 500 mM and more preferably from approximately 5 mM to approximately 50 mM. While particular concentrations of the anodic as well as cathodic materials have been provided, it will be understood that the desired concentration may vary greatly depending upon the geometric configuration of the chamber containing electrochromic medium 124.

For purposes of the present disclosure, the solvent of the electrochromic medium may comprise any one of a number of materials including sulfolane, glutaronitrile, dimethyl sulfoxide, dimethyl formamide, acetonitrile, ethoxyethanol, tetraglyme and other similar polyethers, nitrites, such as 3-hydroxypropionitrile, hydroacrylonitrile, 2-methylglutaronitrile, 2-acetylbutyrolactone, cyclopentanone, cyclic esters including gamma-butyrolactone, propylene carbonate, ethylene carbonate and homogenous mixtures of the same. While specific solvents have been disclosed as being associated with the electrochromic medium, numerous other solvents are likewise contemplated for use.

In a first embodiment of the invention, the additive is more easily reduced than the cathodic material, and, during normal operation of the electrochromic device, serves to substantially preclude the formation of a residual reduced cathodic material while the device is in its high transmission state. The term “high transmission state” is defined as the bleached state, the unpowered state, the unactivated state and/or the open circuit state of the electrochromic device, or a state where it is desirous for the electrochromic medium within the device to be colorless or nearly colorless. As previously discussed, a residual reduced cathodic material can form from any one of a number of different reasons, and can leave the electrochromic medium undesirably tinted or colored, when it is desirous for the electrochromic medium to be colorless or nearly colorless.

In this first embodiment of the invention, the additive may comprise an oxidized form of the anodic material, or alternatively, the additive may comprise an additional material (other than the anodic material) present in an oxidized form. Preferably, the additive comprises a redox potential between that of both the anodic and cathodic materials. For example, the additive may comprise one or more materials such as ferrocinium salts, substituted ferrocinium salts, phenazinium salts, and substituted phenazinium salts. Specific materials may include, for example, di-tert-butyl-diethylferrocinium tetrafluoroborate, (6-(tetra-tert-butylferrocinium)hexyl)triethylammonium di-tetrafluoroborate, (3-(tetra-tert-butylferrocinium)propyl)triethylammonium di-tetrafluoroborate, 5-methylphenazinium tetrafluoroborate. Preferably the concentration of the additive ranges from approximately 0.01 mM to approximately 10 mM.

In a second embodiment of the invention, the additive comprises a reduced form of the cathodic material, and, during normal operation of the electrochromic device, serves to substantially preclude the formation of a residual oxidized anodic material while the device is in its high transmission state. Examples of suitable cathodic materials and their associated reduced species may include, for example, those identified below:

Cathodic Material Additive [Ru(NH₃)₆]³⁺ [Ru(NH₃)₆]²⁺ [Fe(CN)₆]³⁻ [Fe(CN)₆]⁴⁻ [Cr(bpy*)₃]³⁺ [Cr(bpy*)₃]²⁺ [PMo₁₂O₄₀**]³⁻ [PMo₁₂O₄₀**]⁴⁻ *wherein bpy is a bipyridine based ligand **wherein PMo₁₂O₄₀ is a polyoxometalate complex

It will be understood that only the electrochemically relevant portion of the complexes have been disclosed and that the above-identified complexes can be associated with any one of a number of cations or anions to form a neutral species. Preferably the concentration of the additive ranges from approximately 0.01 mM to approximately 10 mM.

In a third embodiment of the invention, the additive is more easily oxidized than the anodic material and is preferably selected from one or more materials, such as substituted ferrocenes, substituted ferrocenyl salts, and mixtures thereof. During normal operation of the electrochromic device, the additives comprising the third embodiment serve to substantially preclude the formation of a residual oxidized anodic material while the device is in its high transmission state. Specific examples of suitable materials include di-tert-butyl-diethylferrocene, (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate, and (3-(tetra-tert-butylferrocenyl)propyl)triethylammonium tetrafluoroborate. While specific materials have been disclosed, for illustrative purposes only, numerous other materials that would be known to those having ordinary skill in the art having the present disclosure before them are likewise contemplated for use. Preferably the concentration of these additives ranges from approximately 0.01 mM to approximately 10 mM.

In a fourth embodiment of the invention, the additive comprises a first component that is more easily reduced than the cathodic material and a second component that is more easily oxidized than the anodic material. During normal operation of the electrochromic device, the first component serves to substantially preclude the formation of a residual reduced cathodic material and the second component serves to substantially preclude the formation of a residual oxidized anodic material while the device is in its high transmission state.

The first additive component may comprise either an oxidized form of the anodic material, or an additional electroactive material present in an oxidized form—or both with appropriate control of additive stoichiometry. Examples of suitable first components include ferrocinium salts, substituted ferrocinium salts, phenazinium salts, and substituted phenazinium salts. Specific materials may include, for example, di-tert-butyl-diethylferrocinium tetrafluoroborate, (6-(tetra-tert-butylferrocinium)hexyl)triethylammonium di-tetrafluoroborate, (3-(tetra-tert-butylferrocinium)propyl)triethylammonium di-tetrafluoroborate, and 5-methylphenazinium tetrafluoroborate.

The second additive component may comprise one or more materials, such as substitutcd phenazines, substituted ferrocenes, substituted ferrocenyl salts, and mixtures thereof. Specific materials may include, for example, 5-methylphenazine, (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate, (3-(tetra-tert-butylferrocenyl)propyl)triethylammonium tetrafluoroborate, di-tert-butyl-diethylferrocene, and mixtures thereof. Preferably the concentration of both the first and second components each ranges from approximately 0.01 mM to approximately 10 mM.

It should be noted that the anodic and cathodic materials can be combined or linked by a bridging unit as described in International Application Serial No. PCT/WO97/EP498 entitled “Electrochromic System.” It is also possible to link the anodic and cathodic materials by other conventional methods.

In addition, the electrochromic medium may also comprise other materials, such as light absorbers, light stabilizers, thermal stabilizers, antioxidants, viscosity modifiers including thickeners, and/or tint providing agents. Suitable UV-stabilizers may include: the material ethyl-2-cyano-3,3-diphenyl acrylate, sold by BASF of Parsippany, N.Y. under the trademark Uvinul N-35 and by Aceto Corp., of Flushing, N.Y. under the trademark Viosorb 910; the material (2-ethylhexyl)-2-cyano-3,3-diphenyl acrylate, sold by BASF under the trademark Uvinul N-539; the material 2-(2′-hydroxy-4′-methylphenyl)benzotriazole, sold by Ciba-Geigy Corp. under the trademark Tinuvin P; the material 2-hydroxy-4-methoxybezophenone sold by American Cyanamid under the trademark Cyasorb UV 9; and the material 2-ethyl-2′-ethoxyalanilide sold by Sandoz Color & Chemicals under the trademark Sanduvor VSU—to name a few. Thickeners include polymethylmethacrylate (PMMA) which is commercially available from, among other chemical suppliers, Aldrich Chemical Co.

It will be understood that during normal operation, the electrochromic devices of the present invention are intended to be cycled between a high transmission state and a low transmission state numerous times while maintaining a colorless or nearly colorless electrochromic medium during the high transmission state relative to an electrochromic medium without the additive.

Electrochromic devices having as a component part a color-stabilized electrochromic medium can be used in a wide variety of applications wherein the transmitted or reflected light can be modulated. Such devices include rear-view mirrors for vehicles; windows for the exterior of a building, home or vehicle; skylights for buildings including tubular light filters; windows in office or room partitions; display devices; contrast enhancement filters for displays; light filters for photographic devices and light sensors; and indicators for power cells as well as primary and secondary electrochemical cells.

The electrochromic media of the present invention utilize many different materials. The preparation and/or commercially available sources are provided herein, unless the material is well known in the art. It will be understood that, unless specified otherwise, the starting reagents are commercially available from Aldrich Chemical Co., Milwaukee, Wis. and other common chemical suppliers. It will be understood that conventional chemical abbreviations will be used when appropriate including the following: grams (g); milliliters (ml); moles (mol), millimoles (mmol), molar (M), and millimolar (mM).

Synthesis of (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate

The synthesis of (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate is a three step synthesis. First, 6-bromo-1-(tetra-tert-butylferrocenyl)-2-hexanone is prepared. Second, the ketonic product is converted to 6-bromo-1-(tetra-tert-butylferrocenyl)hexane, which in turn, is subsequently converted into (6-(tetra-tertbutylferrocenyl)hexyl)triethylammonium tetrafluoroborate.

Preparation of 6-bromo-1-(tetra-tert-butylferrocenyl)-2-hexanone

First, a nitrogen purged flask was charged with 350 ml of dichloroethane, 50.0 g (122 mmol) of tetra-tert-butylferrocene (prepared according to T. Leigh, J. Am. Chem. Soc. 1964, 3294-3302), and 19.3 ml (126 mmol) of 6-bromohexanoyl chloride. Second, the solution was cooled to 0 degrees centigrade, whereupon 13.3 g (100 mmol) of AlCl₃ was charged into the reaction vessel in 3 equal portions at two hour intervals. It will be understood that the freshness and/or purity of the AlCl₃ can impact the degree of substitution of, for example, tert-butyl groups on a cyclopentadienyl ligand. Third, the reaction mixture was then slowly poured into 300 ml of agitating H₂O. Fourth, the organic-aqueous mixture was charged with a sufficient quantity of diethyl ether so that an organic layer was appreciably formed on top of the aqueous layer. Fifth, 50 ml of concentrated hydrochloric acid (HCl) was charged into the vessel. Sixth, approximately 2-5 g of zinc dust was charged into the vessel to reduce any ferrocinium species present in the aqueous layer to the ether soluble ferrocene. Once the layers were clearly defined, they were separated and the aqueous layer was extracted with 200 ml of diethyl ether (Et₂O). The two organic portions were combined and washed with NaHCO₃ and brine. Next the organic solution was dried over MgSO₄. The organic solution was then decanted from the MgSO₄ and filtered. Next, the solvent was removed by rotary evaporation to yield a red oil. The red oil was applied to a vacuum assisted silica gel column and washed with hexane to remove any residual ferrocene. The product was eluted with Et₂O. Upon solvent removal and cooling in a freezer, 64.29 g of 6-bromo-1-(tetra-tert-butylferrocenyl)-2-hexanone was isolated as a red solid.

Preparation of 6-bromo-1-(tetra-tert-butylferrocenyl)hexane

First, 2.27 g (17.02 mmol) of AlCl₃ was dissolved in 200 ml of dry Et₂O in a Schlenk flask under controlled, positive nitrogen pressure. Second, the solution was cooled to 0 degrees centigrade and 17.0 g (17.0 mmol) of 1.0 M LiAlH₄ was charged into the flask via syringe. The resulting suspension was warmed to room temperature and agitated for approximately 15 minutes. Next, 10.00 g (17.02 mmol) of the above prepared 6-bromo-1-(tetra-tert-butylferrocenyl)-2-hexanone was slowly added to the suspension. Once the addition of the ketonic product was complete, the solution was heated to reflux for approximately 3 hours, after which time the solution was cooled to room temperature. The reaction was then quenched by slowly adding H₂O to the solution. When no further exothermic reaction was observed, 250 ml of H₂O was added to dilute the solution. The solution was then transferred to a separatory funnel, whereupon the organic layer was collected and the aqueous layer was extracted with 100 ml of Et₂O. The organic portions were combined and then washed with NaHCO₃ and brine. Next, the solution was dried over MgSO₄. The solution was then decanted from the drying agent and filtered. Next, the solvent was removed via rotary evaporation yielding a yellow-orange oil. The oil was dissolved in a small amount of hexane, applied to a vacuum assisted gel column, and eluted with more hexane. Upon solvent removal, 8.73 g of 6-bromo-1-(tetra-tert-butylferrocenyl)hexane was isolated as a yellow-orange solid.

Preparation of (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate

First, 87.5 ml (628 mmol) of triethylamine (NEt₃), and 53.1 g (92.6 mmol) of 6-bromo-1-(tetra-tert-butylferrocenyl)hexane, and 50 ml of acetonitrile were charged into a reaction vessel. The solution was then heated to reflux for 4 days. During this time the reaction was periodically monitored by thin layer chromatography (TLC), using hexane as the eluent, for the disappearance of the starting material. After cooling to room temperature, the solvent was removed by rotary evaporation and the product was precipitated by addition of Et₂O. The bromide salt of the product was collected on a filter frit, and washed with several portions of cold Et₂O. Next, the salt was dried in vacuo to yield an orange solid. An anion exchange was then performed by dissolving NaBF₄ in water and subsequently removing residual solid particles via filtration. Next the bromide salt of the product was dissolved in Methanol (MeOH) and the NaBF₄ dissolved in water was added to the bromide salt solution. The methanol was slowly removed via rotary evaporation until the product began to precipitate. The orange precipitate was collected on a filter frit, and the recrystallization process was repeated. Finally the precipitate was dissolved in a minimum amount of MeOH, and Et₂O was added slowly to precipitate (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium tetrafluoroborate, an orange solid, which was collected on a frit, dried in vacuo, and stored for later use.

It will be understood that shorter and longer alkyl chain substituted groups, such as a propyl alkyl chain derivative can likewise be synthesized using shorter or longer alkyl chain precursor reagents.

Synthesis of (6-(tetra-tert-butylferrocinium)hexyl)triethylammonium di-tetrafluoroborate

First, 10.00 g (14.67 mmol) of the above-prepared (6-(tetra-tert-butylferrocenyl)-hexyl)triethylammonium tetrafluoroborate was dissolved in 150 ml of dichloromethane (CH₂Cl₂). Next 5.0 g (25.7 mmol) of AgBF₄ was added in 2 equal portions at a 5 minute interval. After agitating for 30 minutes, the solution was filtered and the solvent was removed by rotary evaporation, yielding a green solid. The green solid was redissolved in a minimal amount of CH₂Cl₂ and the product was precipitated by the addition of Et₂O. The solid was dried in vacuo to yield 10.57 g of (6-(tetra-tert-butylferrocinium)hexyl)-triethylammonium tetrafluoroborate as a dark green, crystalline solid.

Synthesis of Di-tert-butyl-diethylferrocene

First, a reaction flask was thoroughly purged with nitrogen and charged with 300 ml of dichloroethane, 10.0 g (33.53 mmol) of di-tert-butylferrocene (prepared according to T. Leigh, J. Am. Chem. Soc. 1964, 3294-3302), and 7.44 ml (100.6 mmol) of freshly distilled acetyl bromide. The solution was agitated, cooled to 0 degrees centigrade, and charged with 8.94 g (67.06 mmol) of AlCl₃. The solution was held at 0 degrees centigrade for one hour and then warmed to room temperature. Agitation was maintained throughout the holding and warming periods. The reaction mixture was then transferred into a beaker containing a mixture of agitating ice and dilute HCl. Next, Et₂O was added to form an organic layer on top of the aqueous layer. The organic layer was separated—via separatory funnel and the aqueous layer was extracted with 200 ml of Et₂O. The organic portions were combined and washed with NaHCO₃ and brine and then dried over MgSO₄. Next, the solution was decanted from the MgSO₄ and placed on a rotary evaporator to remove the solvent, which yielded a red oil. The red oil was applied to a silica gel column and washed with hexane to strip any residual starting material from the product. The ketonic product was then eluted with a mixture of ethyl acetate (EtOAc)/hexane (30:70 by vol.) Upon solvent removal, 5.55 g of di-tert-butyl-diacetylferrocene was collected.

After the di-tert-butyl-diacetylferrocene was prepared, a Schlenk flask under positive nitrogen pressure was charged with 25 ml of dry Et₂O. Second 0.35 g (2.61 mmol) of AlCl₃ was charged into the reaction flask. Agitation was initiated and the AlCl₃ dissolved into solution. Third, 5.23 ml (5.23 mmol) of 1M LiAlH₄ in Et₂O was charged into the reaction flask via syringe. The resulting suspension was agitated for approximately 15 minutes. Fourth, 1.00 g (2.62 mmol) of the above-prepared di-tert-butyl-diacetylferrocene was slowly charged into the reaction vessel. Next, the solution was heated to reflux for approximately 3 hours and then cooled to room temperature overnight with continuous agitation. The reaction was then quenched by the slow addition of Et₂O to the solution. The organic layer was separated from the aqueous layer—via separatory funnel. Next, the aqueous layer was extracted with 100 ml of wet Et₂O. The organic portions were combined and washed with H₂O and brine, which was followed by drying over MgSO₄. The solution was decanted from the drying agent and filtered. Next the solvent was stripped via rotary evaporation, which yielded a yellow-orange oil. The oil was dissolved in a small amount of hexane, applied to a vacuum assisted silica gel column, and eluted with more hexane. Upon solvent removal, 0.627 g of di-tert-butyl-diethylferrocene was collected and stored for later use.

Synthesis of Di-tert-butyl-diethylferrocinium tetrafluoroborate

First, 0.50 g (1.41 mmol) of the above-prepared di-tert-butyl-diethylferrocene, 20 ml of CH₂Cl₂, and 0.282 g (1.45 mmol) of AgBF₄ were charged into a reaction vessel, whereupon agitation was initiated. After approximately 2 hours of agitation, the solution was filtered and the solvent was removed by rotary evaporation, yielding a green solid. The green solid was recrystallized by layered, solvent diffusion of Et₂O into a concentrated solution of crude di-tert-butyl-diethylferrocinium BF₄ in CH₂Cl₂. The solid was dried under vacuum to yield 0.51 g of di-tert-butyl-diethylferrocinium BF₄ as a dark green, crystalline solid.

In support of the present invention, several experiments were conducted wherein electrochromic devices were prepared which comprised a color-stabilizing additive, the color-stabilized performance of which were compared to analogous devices fabricated without a color-stabilizing additive.

In discussing colors it is useful to refer to the Commission Internationale de I'Eclairage's (CIE) 1976 CIELAB Chromaticity Diagram (commonly referred to the La*b* chart). The technology of color is relatively complex, but a fairly comprehensive discussion is given by F. W. Billmeyer and M. Saltzman in Principles of Color Technology, 2^(nd) Ed., J. Wiley and Sons Inc. (1981), and the present disclosure, as it relates to color technology and terminology generally follows that discussion. On the La*b* chart, L defines lightness, a* denotes the red/green value and b* denotes the yellow/blue value. Each of the electrochromic media has an absorption spectra at each particular voltage that may be converted into a three number designation, their La*b* values. However, for the present discussion, the a* and b* values are most relevant inasmuch as: (1) a medium with an increased a* value is more red; (2) a medium with a decreased a* value is more green; (3) a medium with an increased b* value is more yellow; and (4) a medium with a decreased b* value is more blue.

It will be understood that in each of the experiments provided below, the electrochromic materials were dissolved in propylene carbonate (PC).

Experiment No. 1

In this experiment two electrochromic media were prepared by mixing the following materials together in the concentrations provided below:

Experiment No. 1A Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 5,10-Dimethylphenazine 26.5 mM Additive None — UV-Stabilizer T-butylpentylester of Tinuvin P* 50.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt. *a.k.a. 3-[3-(2H-benzotriazole-2-yl)-5-(1,1-dimethylethyl)-4-hydroxyphenyl]propionic acid pentyl ester

Experiment No. 1B Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 5,10-Dimethylphenazine 26.5 mM Additive (6-(tetra-tert-butylferrocenyl)hexyl)tri-  5.0 mM ethylammonium BF₄ UV-Stabilizer T-butylpentylester of Tinuvin P 50.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Each of the media were associated with an electrochromic mirror for testing. Specifically, the mirror comprised two 2×5 inch substrates. The first substrate was coated with generally clear, conductive fluorine doped tin oxide, and the second was coated with fluorine doped tin oxide with a silver reflector on rear surface (114″). The substrates were spaced 137 microns apart for accommodating the medium.

As can be seen, Experiment No. 1A does not include an additive and Experiment No. 1B comprises (6-(tetra-tert-butylferrocenyl)hexyl)triethylammonium BF₄ as an additive. In order to simulate a harsh oxidative environment, each of the above-prepared media were placed into a conventional autoclave with an oxygen input line at 400 p.s.i. at ambient temperature. The media were then evaluated for their color stability by obtaining La*b* values at predetermined intervals. The La*b* data for Experiment Nos. 1A and 1B are provided below.

Experiment No. 1 - Autoclave Experiment No. 1A Experiment No. 1B Hours L a* b* Hours L a* b* 0 88.93 −5.25 8.59 0 89.22 −4.78 9.35 168 89.25 −5.44 8.64 168 89.52 −4.9 9.3 336 89.07 −5.97 9.85 336 89.31 −5.04 9.69 504 88.94 −6.49 11.18 504 89 −5.27 10.44 672 88.39 −7.44 14.11 672 88.81 −5.82 12.25 840 87.72 −8.34 17.76 840 88.48 −6.47 14.87 1008 87.41 −8.37 19.06 1008 88.41 −6.4 15.38 1176 87.1 −8.84 20.99 1176 88.26 −6.44 16.09 1344 86.9 −8.44 21.29 1344 87.96 −6.34 16.4 1512 86.57 −8.44 22.2 1512 87.66 −6.4 16.92 1680 86.2 −8.44 23.58 1680 87.17 −6.81 18.49 1848 85.53 −8.97 25.68 1848 87.01 −6.79 19.11 2016 84.84 −10.01 28.97 2016 86.61 −6.67 19.47

Overall, the medium without the additive is turning substantially more green, which is shown FIG. 2 as an increasing negative a* value and in FIG. 3 as an increasing b* value. Therefore, Experiment No. 1 verifies that, indeed, the usage of the above-identified additive provides and effective mechanism to minimize the adverse coloration effects associated with oxidative environments.

Experiment No. 2

In this experiment four electrochromic media were prepared by mixing the following materials together in the concentrations provided below:

Experiment No. 2A Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 3,7,10-trimethylphenothiazine 26.5 mM Additive None — UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Experiment No. 2B Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 3,7,10-trimethylphenothiazine 26.5 mM Additive (6-(tetra-tert-butylferrocenyl)hexyl)tri-  2.0 mM ethylammonium BF₄ UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Experiment No. 2C Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 3,7,10-trimethylphenothiazine 26.5 mM Additive (6-(tetra-tert-butylferrocinium)hexyl)tri-  2.0 mM ethylammonium (BF₄)₂ UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Experiment No. 2D Component Material Concentration Cathodic Octylviologen BF₄ 34.0 mM Anodic 3,7,10-trimethylphenothiazine 26.5 mM First Additive (6-(tetra-tert-butylferrocenyl)hexyl)-  2.0 mM triethylammonium BF₄ Second Additive (6-(tetra-tert-butylferrocinium)hexyl)-  2.0 mM triethylammonium (BF₄)₂ UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

As can be seen, Experiment No. 2A does not include an additive and Experiment Nos. 2B-2D comprise different ferrocene complexes as additives. Each of the media (2A-2D) were associated with an electrochromic mirror similar in construction to those described in Experiment No. 1 for color stabilization testing. Duplicate sets of mirrors were constructed, half of which were placed in an autoclave under the same conditions identified in Experiment No. 1, while the other half were stored at 85 degrees centigrade to simulate exposure to prolonged elevated temperatures. The La*b* data was collected at predetermined intervals, which is provided below.

Experiment No. 2 - Autoclave Hours L a* b* Hours L a* b* Experiment No. 2A Experiment No. 2B 0 88.44 −3.45 7.76 0 88.8 −3.54 7.81 168 88.81 −3.46 7.67 168 88.93 −3.62 7.7 336 88.67 −3.63 8.19 336 88.8 −3.73 7.78 504 88.62 −3.49 8.28 504 88.9 −4 7.7 672 87.86 −3.75 9.82 672 88.75 −4.25 7.83 840 86.76 −3.35 10.94 840 88.28 −4.21 8.2 1008 86.45 −3.31 12.04 1008 88.04 −4.53 8.89 1176 86.33 −3.92 13.45 1176 87.78 −4.96 10.07 1344 86.01 −4.03 14.76 1344 87.8 −5.59 12.3 1512 85.71 −4.1 15.67 1512 87.4 −5.82 13.93 1680 84.64 −2.99 15.62 1680 87.41 −6.12 14.96 1848 83.59 −1.68 15.15 1848 87.21 −6.39 16.33 2016 82.44 0.08 14.36 2016 87.13 −6.77 17.93 2184 81.42 0.75 14.09 2184 86.95 −6.82 18.79 2352 80.99 2 13.55 2352 86.58 −6.42 18.89 Experiment No. 2C Experiment No. 2D 0 88.16 −4.35 8.16 0 88.38 −3.96 8.15 168 88.5 −4.46 8.26 168 88.51 −3.87 7.95 336 88.15 −4.46 8.51 336 88 −3.82 7.94 504 88.06 −4.5 8.86 504 88.4 −3.9 7.93 672 87.46 −4.76 9.83 672 87.67 −4.09 8.66 840 86.98 −4.88 10.87 840 87.15 −3.98 9.26 1008 86.71 −5.15 11.92 1008 87 −4.07 10.02 1176 86.51 −5.54 13.25 1176 86.47 −4.23 11.34 1344 85.61 −4.45 13.02 1344 86.17 −4.35 12.6 1512 84.66 −3.16 12.62 1512 85.93 −4.53 13.63 1680 82.3 −0.54 11.5 1680 85.45 −4.77 14.32 1848 81.94 0.51 11.28 1848 85.93 −5.21 15.21 2016 80.37 2.3 10.63 2016 85.96 −5.6 16.31 2184 80.33 2.72 10.73 2184 85.9 −5.74 17.25 2352 79.46 3.91 10.46 2352 86.05 −5.81 17.61

Experiment No. 2 - Thermal Hours L a* b* Hours L a* b* Experiment No. 2A Experiment No. 2B 0 88.3 −3.86 8.67 0 88.55 −3.98 8.49 167 87.34 −3.81 6.99 167 86.76 −4.41 6.15 314 83.04 −5.69 1.29 314 82.74 −6.25 0.72 478 79.62 −6.73 −2.58 478 81.28 −6.65 −1.07 651 77.62 −7.54 −5.35 651 80.37 −7.06 −2.23 840 77.43 −7.3 −5.58 840 81.15 −6.63 −1.07 1025 75.06 −8.05 −8.39 1025 80.54 −6.91 −1.35 1193 75.34 −7.86 −7.75 1193 80.53 −6.78 −1.37 1375 75.65 −8.24 −7.41 1375 80.03 −7.06 −1.98 1543 74.97 −7.98 −8.44 1543 79.88 −6.92 −2.29 1785 74.44 −7.93 −8.74 1785 79.75 −6.98 −2.22 1972 74.28 −8.06 −8.19 1972 78.95 −7.27 −3.07 2261 74.94 −7.56 −8.03 2261 79.17 −7.03 −2.95 Experiment No. 2C Experiment No. 2D 0 87.88 −5.14 9.26 0 88.26 −4.46 8.73 167 88.04 −4.34 8.16 167 88.35 −4.05 8.17 314 88.06 −4.21 8.11 314 88.28 −3.91 8.09 478 87.98 −4.11 8.02 478 88.2 −3.92 7.97 651 87.94 −4.03 8.06 651 88.06 −3.96 7.8 840 87.86 −3.94 7.94 840 87.68 −4.06 7.41 1025 87.8 −3.88 8.19 1025 87.26 −4.26 7.03 1193 87.76 −3.92 8.19 1193 87.07 −4.42 6.79 1375 87.81 −3.9 8.29 1375 86.49 −4.61 6.32 1543 87.72 −3.83 8.12 1543 86.54 −4.57 6.1 1785 87.61 −3.87 8.15 1785 86.28 −4.59 6.1 1972 87.63 −3.82 8.23 1972 86.16 −4.87 5.72 2261 87.58 −3.74 8.06 2261 85.86 −4.56 5.75

In reference to the autoclave experiment, FIG. 4 depicts that the media without the ferrocenyl additive (Autoclave Exp. 2A,2C) are turning more red (the positive a* value) than the media with the ferrocenyl additive (Autoclave Exp. 2B-2D). FIG. 5 graphically indicates the b* values for the media (Thermal Exp. 2A-2D) that were associated with mirrors stored at an elevated temperature. In particular, the media comprising a ferrocinium additive (Thermal Exp. 2C,2D) do not appreciably decrease in b* value. In comparison, the media without the ferrocinium additive begin to “fail” or turn blue almost immediately.

In addition, FIGS. 4 and 5 collectively demonstrate that a medium comprising both ferrocenyl as well as ferrocinium species maintains relatively constant a* and b* values in both oxidative and prolonged elevated temperature environments.

Experiment No. 3

In this experiment two electrochromic media were prepared by mixing the following materials together in the concentrations provided below:

Experiment No. 3A Component Material Concentration Cathodic Methylviologen BF₄ 34.0 mM Anodic (6-(tetra-tert-butylferrocenyl)hexyl)tri- 21.8 mM ethylammonium BF₄ Additive None — UV-Stabilizer T-butylpentylester of Tinuvin P 50.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Experiment No. 3B Component Material Concentration Cathodic Methylviologen BF₄ 34.0 mM Anodic (6-(tetra-tert-butylferrocenyl)hexyl)tri- 21.8 mM ethylammonium BF₄ Additive (6-(tetra-tert-butylferrocinium)hexyl)tri-  2.0 mM ethylammonium (BF₄)₂ UV-Stabilizer T-butylpentylester of Tinuvin P 50.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

As can be seen, Experiment No. 3A does not include an additive and Experiment No. 3B comprises (6-(tetra-tert-butylferrocinium)hexyl)triethyl-ammonium BF₄ as an additive. The media from Experiments 3A and 3B were placed into electrochromic windows configured similar to the mirrors as disclosed in Experiment No. 2, except that a reflector was not associated with the rear surface (114″) of the second substrate and the cell spacing was 250 microns instead of 137 microns. The windows were stored at 85 degrees centigrade and La*b* data was collected at predetermined intervals, which is provided below.

Experiment No. 3 - Thermal Experiment No. 3A Experiment No. 3B Hours L a* b* Hours L a* b* 0 81.15 −4.01 19.45 0 80.28 −5.44 19.85 267 81.18 −3.71 19.60 267 80.33 −5.15 20.07 530 80.75 −3.88 19.12 530 80.24 −5.05 20.34 677 79.66 −4.39 17.55 677 80.24 −4.98 20.11 841 78.68 −4.88 16.30 841 80.29 −5.02 20.20 1014 77.44 −5.36 14.04 1014 80.19 −4.78 20.35 1203 76.98 −5.77 13.58 1203 80.30 −5.03 20.16 1388 74.86 −6.45 10.64 1388 80.12 −4.74 20.48 1556 75.07 −6.60 10.91 1556 80.32 −4.89 20.27 1738 73.85 −6.96 9.21 1738 80.27 −4.71 20.28 1906 73.65 −6.96 9.12 1906 80.20 −4.82 20.70 2148 73.13 −7.30 8.02 2148 80.20 −4.76 20.53 2335 71.31 −7.60 5.98 2335 79.82 −4.28 20.68 2624 71.30 −7.77 5.65 2624 79.80 −4.64 20.77

As is shown in both FIGS. 6 and 7, the medium with the ferrocinium complex (Exp. 3B) is substantially more thermally stable than the analogous medium without the additive (Exp. 3A). In fact, the medium without the additive fails “blue” almost immediately (as indicated by the decreasing b* values).

Experiment No. 4

In this experiment two electrochromic media were prepared by mixing the following materials together in the concentrations provided below. Experiment 4A is void of an additive.

Experiment No. 4A Component Material Concentration Cathodic Methylviologen BF₄ 16.0 mM Anodic Di-tert-butyl-diethylferrocene 16.0 mM Additive None — UV-Stabilizer Tinuvin 384 90.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

Experiment No. 4B Component Material Concentration Cathodic Methylviologen BF₄ 16.0 mM Anodic Di-tert-butyl-diethylferrocene 16.0 mM Additive Di-tert-butyl-diethylferrocinium BF₄  2.0 mM UV-Stabilizer Tinuvin 384 90.0 mM UV-Stabilizer Tinuvin P 30.0 mM Thickener PMMA 3% by wt.

The above-prepared media were associated with electrochromic windows constructed and tested analogous to those used in Experiment No. 3, and La*b* data was collected at predetermined intervals, which is provided below.

Experiment No. 4 - Thermal Experiment No. 4A Experiment No. 4B Hours L a* b* Hours L a* b* 0 81.81 −5.43 16.55 0 79.76 −6.60 17.34 270 77.86 −7.61 10.32 270 79.59 −6.13 17.37 487 77.43 −8.84 7.99 487 81.44 −6.07 18.34 753 75.61 −8.77 6.64 753 80.18 −5.78 17.35 921 74.29 −8.76 5.49 921 79.50 −5.55 17.23 1185 72.43 −9.49 2.84 1185 79.53 −5.53 17.36 1448 71.85 −9.73 2.08 1448 79.62 −5.48 17.49 1595 71.07 −9.92 1.17 1595 79.63 −5.43 17.52 1759 70.90 −9.95 0.97 1759 79.60 −5.46 17.41 1932 69.82 −10.45 −0.52 1932 79.75 −5.40 17.64 2121 70.74 −9.82 0.78 2121 79.49 −5.44 17.24 2306 69.51 −10.26 −0.77 2306 79.51 −5.32 17.60 2484 69.38 −10.31 −1.13 2484 79.56 −5.40 17.43 2666 68.65 −10.58 −2.11 2666 79.75 −5.32 17.55 2834 68.47 −10.51 −2.24 2834 79.55 −5.36 17.47 3076 68.34 −10.43 −2.36 3076 79.33 −5.30 17.46 3263 68.23 −10.61 −2.30 3263 79.54 −5.10 17.90 3552 67.66 −10.33 −3.00 3552 79.22 −5.16 17.52 3775 66.81 −10.70 −4.43 3775 79.46 −5.09 17.50

FIGS. 8 and 9 graphically demonstrate that, once again, the medium without the additive (Exp. 4A) begins to fail rapidly relative to the medium comprising the additive.

As can be seen from the above-provided experiments, the incorporation of one or more of the disclosed additives substantially improves the color-stability of an electrochromic medium—even under oxidative environments or elevated temperatures.

While the invention has been described in detail herein in accordance with certain preferred embodiments thereof, many modifications and changes therein may be effected by those skilled in the art. Accordingly, it is our intent to be limited only by the scope of the appending claims and not by way of details and instrumentalities describing the embodiments shown herein. 

What is claimed is:
 1. An electrochromic medium for use in a normally operating electrochromic device, comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) a color-stabilizing additive, wherein the color-stabilizing additive is more easily reduced than the cathodic material, and wherein the color-stabilizing additive is not strongly colored.
 2. The electrochromic medium according to claim 1, wherein the color-stabilizing additive comprises an oxidized form of the anodic material.
 3. The electrochromic medium according to claim 1, wherein the color-stabilizing additive comprises an additional material present in an oxidized form.
 4. The electrochromic medium according to claim 1, wherein the color-stabilizing additive is selected from the group comprising ferrocinium salts, substituted ferrocinium salts, phenazinium salts, substituted phenazinium salts, and mixtures thereof.
 5. The electrochromic medium according to claim 4, wherein the color-stabilizing additive is selected from the group comprising di-tert-butyl-diethylferrocinium tetrafluoroborate, (6-(tetra-tert-butylferrocinium)hexyl)triethylammonium di-tetrafluoroborate, (3-(tetra-tert-butylferrocinium)propyl)triethylammonium di-tetrafluoroborate, 5-methyl-phenazinium tetrafluoroborate, and mixtures thereof.
 6. The electrochromic medium according to claim 1, wherein the concentration of the additive ranges from approximately 0.01 mM to approximately 10 mM.
 7. The electrochromic medium according to claim 1, wherein the cathodic material comprises a viologen.
 8. The electrochromic medium according to claim 1, wherein the concentration of the cathodic material ranges from approximately 1 mM to approximately 500 mM.
 9. The electrochromic medium according to claim 1, wherein the concentration of the cathodic material ranges from approximately 5 mM to approximately 50 mM.
 10. The electrochromic medium according to claim 1, wherein the cathodic material comprises tungsten oxide.
 11. The electrochromic medium according to claim 1, wherein the anodic material is selected from the group comprising ferrocene, substituted ferrocenes, substituted ferrocenyl salts, phenazine, substituted phenazines, phenothiazine, substituted phenothiazines, and mixtures thereof.
 12. The electrochromic medium according to claim 1, wherein the concentration of the anodic material ranges from approximately 1 mM to approximately 500 mM.
 13. The electrochromic medium according to claim 1, wherein the concentration of the anodic material ranges from approximately 5 mM to approximately 50 mM.
 14. An electrochromic medium for use in a normally operating electrochromic device, comprising: (a) an anodic material and a cathodic material, wherein both of the anodic and cathodic materials are electroactive and at least one of the anodic and cathodic materials is electrochromic; and (b) a color-stabilizing additive, wherein the color-stabilizing additive is more easily oxidized than the anodic material, and wherein the color-stabilizing additive is not strongly colored.
 15. The electrochromic medium according to claim 14, wherein the color-stabilizing additive is selected from the group comprising substituted ferrocenes, substituted ferrocenyl salts, and mixtures thereof.
 16. The electrochromic medium according to claim 15, wherein the color-stabilizing additive is selected from the group comprising (6-(tetra-tert-butylferrocenyl)hexyl) triethylammonium tetrafluoroborate, (3-(tetra-tert-butylferrocenyl)propyl) triethylammonium tetrafluoroborate, di-tert-butyl-diethylferrocene and mixtures thereof.
 17. The electrochromic medium according to claim 14, wherein the concentration of the additive ranges from approximately 0.01 mM to approximately 10 mM.
 18. The electrochromic medium according to claim 14, wherein the cathodic material comprises a viologen.
 19. The electrochromic medium according to claim 14, wherein the concentration of the cathodic material ranges from approximately 1 mM to approximately 500 mM.
 20. The electrochromic medium according to claim 14, wherein the concentration of the cathodic material ranges from approximately 5 mM to approximately 50 mM.
 21. The electrochromic medium according to claim 14, wherein the cathodic material comprises tungsten oxide.
 22. The electrochromic medium according to claim 14, wherein the anodic material is selected from the group comprising ferrocene, substituted ferrocenes, substituted ferrocenyl salts, phenazine, substituted phenazines, phenothiazine, substituted phenothiazines, and mixtures thereof.
 23. The electrochromic medium according to claim 14, wherein the concentration of the anodic material ranges from approximately 1 mM to approximately 500 mM.
 24. The electrochromic medium according to claim 14, wherein the concentration of the anodic material ranges from approximately 5 mM to approximately 50 mM.
 25. An electrochromic device comprising: at least one substantially transparent substrate; and an electrochromic medium according to claims 1 or 14 associated with the at least one substantially transparent substrate.
 26. The electrochromic device according to claim 25, comprising a first substantially transparent substrate and a second substrate.
 27. The electrochromic device according to claim 26, wherein the device is an electrochromic window.
 28. The electrochromic device according to claim 26, wherein the second substrate is plated with a reflective material.
 29. The electrochromic device according to claim 28, wherein the reflective material is selected from the group comprising chromium, rhodium, silver, alloys of the same, and mixtures thereof.
 30. The electrochromic device according to claim 29, wherein the device is an electrochromic mirror. 